G-aenial Bond – one component self-etching light-cured adhesive.
For use only by a dental professional in the recommended indications.
1. Bonding of light cured composites and acid modified composites (compomers) to tooth structure.
2. Bonding of dual cured luting and core build up composites to tooth structure as long as these materials are light cured.
- Pulp capping.
- In rare cases the product may cause sensitivity in some people. If any such reactions are experienced, discontinue the use of the product and refer to a physician.
Not to be used
- In combination with chemically cured composite resin.
- In combination with eugenol containing materials as eugenol may hinder G-aenial Bond from setting or bonding properly.
- In combination with desensitizers as desensitizers may hinder G-aenial Bond from setting or bonding properly.
- In combination with dual cured luting and core build up composites in case these materials will not be light cured.
G-aenial Bond – instructions for use
1. Cavity Preparation
Prepare tooth using standard techniques. Make sure that the temporary material is thoroughly removed from the surace. Use rubber dam for protection. Dry the prepared tooth surfaces by gently blowing with an air syringe.
Note: For pulp capping, use calcium hydroxide.
2. Technique Selection
Select out of the following 2 technique options
- Self-etch technique – apply G-aenial Bond to bur cut enamel and dentin, without a separate etching step.
- Selective etching of enamel – prior to applying G-aenial Bond to enamel and dentin, etch (bur cut) enamel with 35-40% phosphoric acid gel for 10 seconds, rinse for 5 seconds and gently dry.
Note: Non bur cut enamel should always be treated with a 35-40% phosphoric acid gel for 10 seconds, rinsed with water for 5 seconds and gently dried.
- Prior to dispensing, shake the bottle of G-aenial Bond thoroughly. Dispense a few drops into a clean dispensing dish. Replace bottle cap immediately after use.
- IMMEDIATELY apply to the prepared enamel and dentin surfaces using the disposable applicator.
- Leave undisturbed for 10 seconds after the end of application.
- Then, dry thoroughly for 5 seconds with oil free air under MAXIMUM air pressure. Use vacuum suction to prevent splatter of the adhesive. The final result should be a thin adhesive film with the appearance of frosted glass and which does not visibly move under further air pressure.
- When removing from refrigerator after long-term storage, leave G-aenial Bond to stand at room temperature for several minutes prior to use.
- Apply G-ænial Bond immediately as the material contains a volatile solvent.
- Remove excess material remaining on the tooth (other than the surfaces to be bonded) using a sponge or cotton pellet as residue material is hard to remove after light curing.
- Should the applied material be contaminated with water, blood or saliva prior to light curing, wash and dry the tooth and repeat the procedure by re-applying material.
4. Light Curing
Light cure using a visible light curing unit.
Halogen / LED (700 mW/cm²) : 10 seconds
Plasma Arc (2000 mW/cm²) : 3 seconds
G-Light (1200 mW/cm²) : 5 seconds
In case where the light guide tip is more than 10mm away from the surface to be irradiated, light cure for the following time.
Halogen / LED (700 mW/cm²) : 20 seconds
Plasma Arc (2000 mW/cm²) : 6 seconds
G-Light (1200 mW/cm²) : 10 seconds
- Light cure completely for an effective bonding strength. Lower light intensity may cause insufficient adhesion.
- Use a protective light shield or similar protective eye wear during light curing.
5A. Placement of light cured composites and compomers
After having light cured the adhesive, follow manufacturer’s instructions for use in order to place, contour and light cure the composite resin material of choice.
5B. Placement of dual cured composites
After having light cured the adhesive, make sure to light cure the dual cured composite material separately. Self curing only will result in insufficient bonding strength.
Adjust restoration, finish and polish using standard techniques.
Store at room temperature (1-28°C) (33.8-82.4°F).
If not in use for a prolonged period of time, store in refrigerator.
Shelf life: 2 years from date of manufacture.
- G-aenial Bond Bottle Kit: 5 mL liquid (1), disposable dispensing dish (20), disposable applicator fine (50)
- G-aenial Bond Bottle Refill: 5 mL liquid (1)
- G-aenial Bond 3-bottle Pack: 5 mL liquid (3)
- G-aenial Bond is flammable. Do not use near naked flame. Keep away from sources of ignition. Do not store large quantities in one area. Keep away from direct sunlight.
- G-aenial Bond is volatile. Use in a well ventilated place. Advise patients to breath through nose.
- In case of contact with eyes, flush immediately with water and seek medical attention.
- In case of contact with oral tissue or skin, immediately remove with a sponge or cotton pellet. After the restorative treatment is finished, rinse thoroughly with water.
- If the tissue contacted by the material turns white or forms a blister, advise the patient to leave the affected area undisturbed, until the mark disappears, usually in 1-2 weeks. To avoid contact, it is recommended to apply cocoa butter to the area where rubber dam cannot cover.
- Avoid inhalation or digestion of material.
- When spilt on the table or floor, immediately wipe off with a dry cloth.
- Do not mix with other products.
- Dispose of all waste according to local regulations.
MANUFACTURED by GC CORPORATION 76-1 Hasunuma-cho, Itabashi-ku, Tokyo 174-8585, Japan
G-BOND – ADVANCED SEVENTH GENERATION BONDING
SCOTCHBOND UNIVERSAL – ADHESIVE 3M ESPE
FUTURABOND U – DUAL-CURE UNIVERSAL ADHESIVE IN SINGLE DOSE DELIVERY SYSTEM
OPTIBOND SOLO PLUS – ADHESIVE SYSTEM KERR
ADPER SINGLE BOND 2 – ADHESIVE 3M ESPE